| category | material id | brinell hardness (HB) | cte per K (1/K) | density kg m3 (kg/m3) | elastic modulus MPa (MPa) | elongation percent (%) | grade | heat treatment | melting point C (°C) | name | notes | poisson ratio (dimensionless) | shear modulus MPa (MPa) | specific heat J kgK (J/(kg·K)) | standard | tensile strength MPa (MPa) | thermal conductivity W mK (W/(m·K)) | yield strength MPa (MPa) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| titanium_alloy | Ti-6Al-4V_Annealed##ASTM##Annealed | 36 | 0.000009 | 4,430 | 114,000 | 14 | Ti-6Al-4V | Annealed | 1,660 | Ti-6Al-4V (Grade 5) Annealed | UNS R56400; ASTM B265/B348; solidus 1604C liquidus 1660C; Brinell per ASTM E10; annealed mill product; widely used aerospace/biomedical alloy; shear mod 44 GPa | 0.342 | 44,000 | 526 | ASTM | 950 | 6.7 | 880 |
| titanium_alloy | Ti-6Al-4V_STA##ASTM##STA | 36 | 0.000009 | 4,430 | 114,000 | 10 | Ti-6Al-4V | Solution Treated & Aged (STA) | 1,660 | Ti-6Al-4V (Grade 5) Solution Treated & Aged | UNS R56400; AMS 4965; solution treat 955C/1hr quench + age 482C/4hr; highest strength condition for structural aerospace use; shear mod 44 GPa | 0.342 | 44,000 | 526 | ASTM | 1,170 | 7.2 | 1,100 |
This is a sample. Search the full metal alloy properties dataset and 300+ more by creating a free account and accessing the database.
Get started for FREE