ATI N-90 vs Haynes 214
Property comparison of ATI N-90 and Haynes 214, both nickel alloy.
| Property | ATI N-90 | Haynes 214 | Difference |
|---|---|---|---|
| Yield strength | 695 MPa | 577 MPa | -17% |
| Tensile strength | 1,080 MPa | 975 MPa | -10% |
| Elongation | 20 % | 37.3 % | +86% |
| Density | 8,110 kg/m³ | 8,050 kg/m³ | -1% |
Difference is Haynes 214 relative to ATI N-90. Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
ATI N-90
- grade
- Ni-Cr-Co (N07090)
- standard
- BS 2HR2
- heat treatment
- Aged (bar)
Haynes 214
- grade
- 214
- standard
- Haynes International Datasheet H-3008
- heat treatment
- Annealed
What else is in Engineering Database
Iron Engine ↗Engineering AI at ironengine.ai
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators