ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, age hardened) vs ATI N-90
Property comparison of ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, age hardened) and ATI N-90, both nickel alloy.
| Property | ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, age hardened) | ATI N-90 | Difference |
|---|---|---|---|
| Yield strength | 621 MPa | 695 MPa | +12% |
| Tensile strength | 1,034 MPa | 1,080 MPa | +4% |
| Elongation | 35 % | 20 % | -43% |
| Density | 8,360 kg/m³ | 8,110 kg/m³ | -3% |
Difference is ATI N-90 relative to ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, age hardened). Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
- grade
- UNS N07263
- standard
- ATI Technical Data Sheet
- heat treatment
- Solution anneal 1038-1177°C + age 802°C/8h AC (AMS 5872E)
- grade
- Ni-Cr-Co (N07090)
- standard
- BS 2HR2
- heat treatment
- Aged (bar)
What else is in Engineering Database
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators