ATI H-N vs ATI H-W
Property comparison of ATI H-N and ATI H-W, both nickel alloy.
| Property | ATI H-N | ATI H-W | Difference |
|---|---|---|---|
| Yield strength | 276 MPa | 517 MPa | +87% |
| Tensile strength | 690 MPa | 966 MPa | +40% |
| Elongation | 40 % | 50 % | +25% |
| Density | 8,770 kg/m³ | 8,990 kg/m³ | +3% |
Difference is ATI H-W relative to ATI H-N. Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
ATI H-N
- grade
- Ni-Mo (N10003)
- standard
- UNS N10003
- heat treatment
- Annealed (bar)
ATI H-W
- grade
- Ni-Mo-Cr (N10004)
- standard
- UNS N10004
- heat treatment
- Annealed (bar)
What else is in Engineering Database
Iron Engine ↗Engineering AI at ironengine.ai
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculatorsRelated comparisons
ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, age hardened)vsATI H-NATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, age hardened)vsATI H-WATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed)vsATI H-NATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed)vsATI H-WATI HB-2vsATI H-NATI H-NvsATI M-252ATI H-NvsATI Moly Permalloy (80Ni-4.4Mo-Fe soft magnetic alloy, annealed)ATI HB-2vsATI H-W