ATI HB-2 vs ATI H-W
Property comparison of ATI HB-2 and ATI H-W, both nickel alloy.
| Property | ATI HB-2 | ATI H-W | Difference |
|---|---|---|---|
| Yield strength | 351 MPa | 517 MPa | +47% |
| Tensile strength | 758 MPa | 966 MPa | +27% |
| Elongation | 45 % | 50 % | +11% |
| Density | 9,210 kg/m³ | 8,990 kg/m³ | -2% |
Difference is ATI H-W relative to ATI HB-2. Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
ATI HB-2
- grade
- Ni-Mo (N10665)
- standard
- ASTM B335
- heat treatment
- Annealed (bar)
ATI H-W
- grade
- Ni-Mo-Cr (N10004)
- standard
- UNS N10004
- heat treatment
- Annealed (bar)
What else is in Engineering Database
Iron Engine ↗Engineering AI at ironengine.ai
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculatorsRelated comparisons
ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, age hardened)vsATI H-WATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, age hardened)vsATI HB-2ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed)vsATI H-WATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed)vsATI HB-2ATI H-NvsATI H-WATI HB-2vsATI H-NATI H-WvsATI M-252ATI H-WvsATI Moly Permalloy (80Ni-4.4Mo-Fe soft magnetic alloy, annealed)