ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed) vs ATI H-N
Property comparison of ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed) and ATI H-N, both nickel alloy.
| Property | ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed) | ATI H-N | Difference |
|---|---|---|---|
| Yield strength | 414 MPa | 276 MPa | -33% |
| Tensile strength | 827 MPa | 690 MPa | -17% |
| Elongation | 50 % | 40 % | -20% |
| Density | 8,360 kg/m³ | 8,770 kg/m³ | +5% |
Difference is ATI H-N relative to ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed). Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
- grade
- UNS N07263
- standard
- ATI Technical Data Sheet
- heat treatment
- Solution anneal 1038-1177°C rapid AC or quench
- grade
- Ni-Mo (N10003)
- standard
- UNS N10003
- heat treatment
- Annealed (bar)
What else is in Engineering Database
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators