ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed) vs ATI HB-2
Property comparison of ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed) and ATI HB-2, both nickel alloy.
| Property | ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed) | ATI HB-2 | Difference |
|---|---|---|---|
| Yield strength | 414 MPa | 351 MPa | -15% |
| Tensile strength | 827 MPa | 758 MPa | -8% |
| Elongation | 50 % | 45 % | -10% |
| Density | 8,360 kg/m³ | 9,210 kg/m³ | +10% |
Difference is ATI HB-2 relative to ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed). Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
- grade
- UNS N07263
- standard
- ATI Technical Data Sheet
- heat treatment
- Solution anneal 1038-1177°C rapid AC or quench
- grade
- Ni-Mo (N10665)
- standard
- ASTM B335
- heat treatment
- Annealed (bar)
What else is in Engineering Database
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators