Nodular-Cast-Iron-Jis-UTS600 — Cast Iron
- Category
- Cast Iron
- Material Id
- Nodular Cast Iron Jis UTS600
- Cte per K (1/K)
- 0.000011
- Density Kg M3 (kg/m3)
- 7,160
- Elastic Modulus MPa (MPa)
- 169,000
- Melting Point C (°C)
- 1,150
- Name
- Nodular Cast Iron
- Poisson Ratio (dimensionless)
- 0.2
- Shear Modulus MPa (MPa)
- 70,000
- Specific Heat J kgK (J/(kg·K))
- 460
- Standard
- Jis
- Tensile Strength MPa (MPa)
- 600
- Thermal Conductivity W mK (W/(m·K))
- 36
- Vickers Hardness (HV)
- 210
- Yield Strength MPa (MPa)
- 370
Source: JIS