ATI HB-2 vs ATI M-252
Property comparison of ATI HB-2 and ATI M-252, both nickel alloy.
| Property | ATI HB-2 | ATI M-252 | Difference |
|---|---|---|---|
| Yield strength | 351 MPa | 620 MPa | +77% |
| Tensile strength | 758 MPa | 1,100 MPa | +45% |
| Elongation | 45 % | 20 % | -56% |
| Density | 9,210 kg/m³ | 8,240 kg/m³ | -11% |
Difference is ATI M-252 relative to ATI HB-2. Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
ATI HB-2
- grade
- Ni-Mo (N10665)
- standard
- ASTM B335
- heat treatment
- Annealed (bar)
ATI M-252
- grade
- Ni-Cr-Co-Mo (N07252)
- standard
- ASTM B637
- heat treatment
- Aged (bar)
What else is in Engineering Database
Iron Engine ↗Engineering AI at ironengine.ai
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculatorsRelated comparisons
ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, age hardened)vsATI HB-2ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, age hardened)vsATI M-252ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed)vsATI HB-2ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed)vsATI M-252ATI HB-2vsATI H-NATI H-NvsATI M-252ATI HB-2vsATI H-WATI H-WvsATI M-252