Haynes-242-Aged — Nickel Alloy
- Category
- Nickel Alloy
- Material Id
- Haynes 242 Aged
- Cte per K (1/K)
- 0.000011
- Density Kg M3 (kg/m3)
- 9,050
- Elastic Modulus MPa (MPa)
- 229,000
- Electrical Resistivity uOhm M (uOhm*m)
- 1.22
- Elongation Percent (%)
- 33.7
- Grade
- 242
- Heat Treatment
- Aged
- Melting Point C (°C)
- 1,333
- Name
- Haynes 242
- Poisson Ratio (dimensionless)
- 0.3
- Specific Heat J kgK (J/(kg·K))
- 386
- Standard
- Haynes International Datasheet H-3079
- Tensile Strength MPa (MPa)
- 1,290
- Thermal Conductivity W mK (W/(m·K))
- 11.3
- Vickers Hardness (HV)
- 271
- Yield Strength MPa (MPa)
- 845
Source: Haynes International Datasheet H-3079