Metal Alloy Properties: nickel alloy
ATI C-263 Annealed to ATI K-500 HotFinished Aged
Metal and alloy mechanical properties — tensile/yield strength, elastic modulus, density, hardness for steels, aluminum alloys, copper alloys, titanium, nickel alloys, cast iron, and more
| category | material id | cte per K (1/K) | density kg m3 (kg/m3) | elastic modulus MPa (MPa) | elongation percent (%) | grade | heat treatment | name | property basis | specific heat J kgK (J/(kg·K)) | standard | tensile strength MPa (MPa) | thermal conductivity W mK (W/(m·K)) | yield strength MPa (MPa) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| nickel alloy | ATI C-263 Annealed | — | 8,360 | 220,000 | 50 | UNS N07263 | Solution anneal 1038-1177°C rapid AC or quench | ATI C-263 (Ni-Co-Cr-Mo precipitation-hardened superalloy, solution annealed) | Typical | — | ATI Technical Data Sheet | 827 | — | 414 |
| nickel alloy | ATI HB2 Bar | — | 9,210 | — | 45 | Ni-Mo (N10665) | Annealed (bar) | ATI HB-2 | Minimum | — | ASTM B335 | 758 | — | 351 |
| nickel alloy | ATI HN Bar | — | 8,770 | — | 40 | Ni-Mo (N10003) | Annealed (bar) | ATI H-N | Minimum | — | UNS N10003 | 690 | — | 276 |
| nickel alloy | ATI HW Bar | — | 8,990 | — | 50 | Ni-Mo-Cr (N10004) | Annealed (bar) | ATI H-W | Minimum | — | UNS N10004 | 966 | — | 517 |
| nickel alloy | ATI K-500 Annealed ATI | 0.000014 | 8,470 | 179,000 | 42 | UNS N05500 | Annealed | ATI K-500 (Monel K-500 Ni-Cu-Al-Ti, annealed) | Typical | 408 | ATI Technical Data Sheet | 620 | 17.4 | 275 |
| nickel alloy | ATI K-500 Annealed Aged | 0.000014 | 8,470 | 179,000 | 22 | UNS N05500 | Annealed + age hardened | ATI K-500 (Monel K-500 Ni-Cu-Al-Ti, annealed and age hardened) | Typical | 408 | ATI Technical Data Sheet | 1,000 | 17.4 | 665 |
| nickel alloy | ATI K-500 ColdDrawn | 0.000014 | 8,470 | 179,000 | 18 | UNS N05500 | Cold drawn (not age hardened) | ATI K-500 (Monel K-500 Ni-Cu-Al-Ti, cold drawn) | Typical | 408 | ATI Technical Data Sheet | 860 | 17.4 | 690 |
| nickel alloy | ATI K-500 ColdDrawn Aged | 0.000014 | 8,470 | 179,000 | 22 | UNS N05500 | Cold drawn + age hardened | ATI K-500 (Monel K-500 Ni-Cu-Al-Ti, cold drawn and age hardened) | Typical | 408 | ATI Technical Data Sheet | 1,175 | 17.4 | 1,000 |
| nickel alloy | ATI K-500 HotFinished | 0.000014 | 8,470 | 179,000 | 47 | UNS N05500 | Hot finished (as-worked, not age hardened) | ATI K-500 (Monel K-500 Ni-Cu-Al-Ti, hot finished) | Typical | 408 | ATI Technical Data Sheet | 690 | 17.4 | 310 |
| nickel alloy | ATI K-500 HotFinished Aged | 0.000014 | 8,470 | 179,000 | 30 | UNS N05500 | Hot finished + age hardened | ATI K-500 (Monel K-500 Ni-Cu-Al-Ti, hot finished and age hardened) | Typical | 408 | ATI Technical Data Sheet | 1,040 | 17.4 | 795 |
What else is in Engineering Database
Iron Engine ↗Engineering AI at ironengine.ai
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators