Cmh17 Fiber Reference: 2.4.1.5(a)
011 to 020
CMH-17/MIL-HDBK-17-3F fiber and reinforcement reference tables. Includes typical fiber properties (carbon, glass, aramid, boron), nominal composite properties for various reinforcement types, fiber sizing/finish compatibility data, and general reference data from MIL-HDBK-17-3F Chapter 2 and CMH-17 Chapter 6.
| table id | row index | c1 | c2 | c3 | context | source page |
|---|---|---|---|---|---|---|
| 2.4.1.5(a) | 011 | Tensile, axial | — | 80 ksi (600 MPa) | MIL-HDBK-17-3F Volume 3, Chapter 2 Materials and Processes - The Effects of Variability on Composite Properties TABLE 2.4.1.5(a) Nominal properties of alumina. Composition > 99% α-Al O Filaments/yarn 200, nominal 2 3 Mel | 72 |
| 2.4.1.5(a) | 012 | Tensile, transverse | — | 26-30 ksi (130-210 MPa) | MIL-HDBK-17-3F Volume 3, Chapter 2 Materials and Processes - The Effects of Variability on Composite Properties TABLE 2.4.1.5(a) Nominal properties of alumina. Composition > 99% α-Al O Filaments/yarn 200, nominal 2 3 Mel | 72 |
| 2.4.1.5(a) | 013 | Shear | — | 12-17 ksi (85-120 GPa) | MIL-HDBK-17-3F Volume 3, Chapter 2 Materials and Processes - The Effects of Variability on Composite Properties TABLE 2.4.1.5(a) Nominal properties of alumina. Composition > 99% α-Al O Filaments/yarn 200, nominal 2 3 Mel | 72 |
| 2.4.1.5(a) | 014 | Fatigue - Axial Endurance Limit | 107 cycles at 75% of static ultimate (tension-tension, R=0.1, and rotating-bending) | — | MIL-HDBK-17-3F Volume 3, Chapter 2 Materials and Processes - The Effects of Variability on Composite Properties TABLE 2.4.1.5(a) Nominal properties of alumina. Composition > 99% α-Al O Filaments/yarn 200, nominal 2 3 Mel | 72 |
| 2.4.1.5(a) | 015 | Average Thermal Expansion | 68-750° (20-400°C) | — | MIL-HDBK-17-3F Volume 3, Chapter 2 Materials and Processes - The Effects of Variability on Composite Properties TABLE 2.4.1.5(a) Nominal properties of alumina. Composition > 99% α-Al O Filaments/yarn 200, nominal 2 3 Mel | 72 |
| 2.4.1.5(a) | 016 | Axial | — | 4.0 µin/in/F° (7.2 µm/m/C°) | MIL-HDBK-17-3F Volume 3, Chapter 2 Materials and Processes - The Effects of Variability on Composite Properties TABLE 2.4.1.5(a) Nominal properties of alumina. Composition > 99% α-Al O Filaments/yarn 200, nominal 2 3 Mel | 72 |
| 2.4.1.5(a) | 017 | Transverse | — | 11 µin/in/F° (20 µm/m/C°) | MIL-HDBK-17-3F Volume 3, Chapter 2 Materials and Processes - The Effects of Variability on Composite Properties TABLE 2.4.1.5(a) Nominal properties of alumina. Composition > 99% α-Al O Filaments/yarn 200, nominal 2 3 Mel | 72 |
| 2.4.1.5(a) | 018 | Thermal Conductivity | 68-750° (20-400°C) | 22-29 Btu/hr-ft-°F (38-50 J/m-s-°C) | MIL-HDBK-17-3F Volume 3, Chapter 2 Materials and Processes - The Effects of Variability on Composite Properties TABLE 2.4.1.5(a) Nominal properties of alumina. Composition > 99% α-Al O Filaments/yarn 200, nominal 2 3 Mel | 72 |
| 2.4.1.5(a) | 019 | Specific Heat | 68-750° (20-400°C) | 0.19-0.12 Btu/lbm-°F (0.8-0.5 J/gm-°C) | MIL-HDBK-17-3F Volume 3, Chapter 2 Materials and Processes - The Effects of Variability on Composite Properties TABLE 2.4.1.5(a) Nominal properties of alumina. Composition > 99% α-Al O Filaments/yarn 200, nominal 2 3 Mel | 72 |
| 2.4.1.5(a) | 020 | Density | — | 0.12 lbm/in3 (3.3 gm/cm3) | MIL-HDBK-17-3F Volume 3, Chapter 2 Materials and Processes - The Effects of Variability on Composite Properties TABLE 2.4.1.5(a) Nominal properties of alumina. Composition > 99% α-Al O Filaments/yarn 200, nominal 2 3 Mel | 72 |
What else is in Engineering Database
Iron Engine ↗Engineering AI at ironengine.ai
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators