Cmh17 Fiber Reference: 2.4.1.7(f)
CMH-17/MIL-HDBK-17-3F fiber and reinforcement reference tables. Includes typical fiber properties (carbon, glass, aramid, boron), nominal composite properties for various reinforcement types, fiber sizing/finish compatibility data, and general reference data from MIL-HDBK-17-3F Chapter 2 and CMH-17 Chapter 6.
| table id | row index | c1 | c2 | c3 | context | source page |
|---|---|---|---|---|---|---|
| 2.4.1.7(f) | 001 | PROPERTY | Room Temperature U.S. SI | 1/2 Hour at 350°F (177°C) U.S. SI | MIL-HDBK-17-3F Volume 3, Chapter 2 Materials and Processes - The Effects of Variability on Composite Properties TABLE 2.4.1.7(f) Typical properties for quartz/polyimide. PROPERTY Room Temperature 1/2 Hour at 350°F (177°C | 80 |
| 2.4.1.7(f) | 002 | Tensile Strength (ksi,MPa) Tensile Modulus (Msi,GPa) Flexural Strength (ksi,MPa) Flexural Modulus (Msi,GPa) Compressive Strength (ksi,MPa) Compressive Modulus (Msi,GPa) Laminate Resin Content (wt%) | 79.1 - 105 545 - 724 3.9 27 93.7 - 102 646 - 703 3.2 22 67.0 - 67.4 462 - 465 3.5 - 3.7 24 - 26 36.2 - 36.2 | 62.4 - 68.3 430 - 471 2.6 - 2.8 18 - 19 38.6 - 45.2 266 - 312 2.8 19 | MIL-HDBK-17-3F Volume 3, Chapter 2 Materials and Processes - The Effects of Variability on Composite Properties TABLE 2.4.1.7(f) Typical properties for quartz/polyimide. PROPERTY Room Temperature 1/2 Hour at 350°F (177°C | 80 |
This is a sample. Search the full cmh17 fiber reference dataset and 350+ more by creating a free account and accessing the database.
Get started for FREE