Ti-2.5Cu (TIMETAL 230) Solution Treated and Aged vs Ti-35Zr-10Nb (ATI Tiadyne 3510) Fully Hardened
Property comparison of Ti-2.5Cu (TIMETAL 230) Solution Treated and Aged and Ti-35Zr-10Nb (ATI Tiadyne 3510) Fully Hardened, both titanium alloy.
| Property | Ti-2.5Cu (TIMETAL 230) Solution Treated and Aged | Ti-35Zr-10Nb (ATI Tiadyne 3510) Fully Hardened | Difference |
|---|---|---|---|
| Yield strength | 600 MPa | 1,034 MPa | +72% |
| Tensile strength | 760 MPa | 1,103 MPa | +45% |
| Elongation | 20 % | 12 % | -40% |
| Elastic modulus | 112,500 MPa | 71,700 MPa | -36% |
| Density | 4,560 kg/m³ | 5,250 kg/m³ | +15% |
| Thermal conductivity | 12.97 W/m·K | 7.58 W/m·K | -42% |
| Coefficient of thermal expansion | 0.000009 1/K | 0.000008 1/K | -16% |
Difference is Ti-35Zr-10Nb (ATI Tiadyne 3510) Fully Hardened relative to Ti-2.5Cu (TIMETAL 230) Solution Treated and Aged. Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
- grade
- Ti-2.5Cu
- standard
- BS TA51 / DTD 5013
- heat treatment
- Solution Treated and Aged
- grade
- Ti-35Zr-10Nb
- standard
- ATI Proprietary
- heat treatment
- Fully Hardened (aged 425-550°C)
What else is in Engineering Database
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators