Haynes 282 vs MAR-M 247 (Ni-8.3Cr-10Co-10W-5.5Al-3Ta-1Ti-0.7Mo) cast heat treated
Property comparison of Haynes 282 and MAR-M 247 (Ni-8.3Cr-10Co-10W-5.5Al-3Ta-1Ti-0.7Mo) cast heat treated, both nickel alloy.
| Property | Haynes 282 | MAR-M 247 (Ni-8.3Cr-10Co-10W-5.5Al-3Ta-1Ti-0.7Mo) cast heat treated | Difference |
|---|---|---|---|
| Yield strength | 699 MPa | 930 MPa | +33% |
| Tensile strength | 1,132 MPa | 1,035 MPa | -9% |
| Elongation | 33 % | 5 % | -85% |
| Density | 8,290 kg/m³ | 7,800 kg/m³ | -6% |
| Thermal conductivity | 10.3 W/m·K | 11.3 W/m·K | +10% |
| Coefficient of thermal expansion | 0.000012 1/K | 0.000013 1/K | +4% |
| Melting point | 1,338 °C | 1,366 °C | +2% |
Difference is MAR-M 247 (Ni-8.3Cr-10Co-10W-5.5Al-3Ta-1Ti-0.7Mo) cast heat treated relative to Haynes 282. Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
- grade
- 282
- standard
- Haynes International Datasheet H-3173
- heat treatment
- Aged (Solution Annealed + Double Aged)
- grade
- N/A
- standard
- AZoM Super Alloy MAR-M 247 (ArticleID 7808); TMS Superalloys 1984 Kaufman et al. MAR-M-247 turbine blisk
- heat treatment
- investment cast + standard heat treat
What else is in Engineering Database
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators