D357.0 vs Leaded Muntz metal C36500
Property comparison of D357.0 and Leaded Muntz metal C36500, both aluminum alloy.
| Property | D357.0 | Leaded Muntz metal C36500 | Difference |
|---|---|---|---|
| Yield strength | 248.22 MPa | 138 MPa | -44% |
| Tensile strength | 310.28 MPa | 372 MPa | +20% |
| Elongation | 2 % | 45 % | +2150% |
| Elastic modulus | 71,708 MPa | 105,000 MPa | +46% |
| Shear modulus | 26,891 MPa | 40,000 MPa | +49% |
| Poisson ratio | 0.33 | 0.32 | -3% |
| Density | 2,685 kg/m³ | 8,800 kg/m³ | +228% |
Difference is Leaded Muntz metal C36500 relative to D357.0. Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
D357.0
- grade
- D357.0
- standard
- MIL-HDBK-5J
- heat treatment
- Cast
Leaded Muntz metal C36500
- grade
- —
- standard
- ANSI
- heat treatment
- As hot rolled
What else is in Engineering Database
Iron Engine ↗Engineering AI at ironengine.ai
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators