Al-Li 2090 vs 2519
Property comparison of Al-Li 2090 and 2519, both aluminum alloy.
| Property | Al-Li 2090 | 2519 | Difference |
|---|---|---|---|
| Yield strength | 482.5 MPa | 406.8 MPa | -16% |
| Tensile strength | 532.5 MPa | 455.07 MPa | -15% |
| Elongation | 2.1 % | 9 % | +329% |
| Elastic modulus | 79,700 MPa | 72,398 MPa | -9% |
| Shear modulus | 30,300 MPa | 27,580 MPa | -9% |
| Poisson ratio | 0.315 | 0.33 | +5% |
| Density | 2,590 kg/m³ | 2,823 kg/m³ | +9% |
Difference is 2519 relative to Al-Li 2090. Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
- grade
- 2090-T61
- standard
- NISTIR 3971
- heat treatment
- T61
- grade
- 2519
- standard
- MIL-HDBK-5J
- heat treatment
- Wrought
About 2xxx aluminum alloys
2xxx aluminum alloys are alloyed with copper. They reach the highest strengths in the wrought aluminum family but corrode faster than 5xxx or 6xxx and are difficult to weld. 2024 is the aerospace standard for skin and structure; 2014 is used for forgings.
What else is in Engineering Database
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators