17 4PH vs ATI 412 Dual-Phase Stainless Steel
Property comparison of 17 4PH and ATI 412 Dual-Phase Stainless Steel, both stainless steel.
| Property | 17 4PH | ATI 412 Dual-Phase Stainless Steel | Difference |
|---|---|---|---|
| Yield strength | 1,000 MPa | 414 MPa | -59% |
| Tensile strength | 1,070 MPa | 565 MPa | -47% |
| Elongation | 12 % | 24 % | +100% |
| Density | 7,750 kg/m³ | 7,750 kg/m³ | 0% |
Difference is ATI 412 Dual-Phase Stainless Steel relative to 17 4PH. Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
- grade
- S17400
- standard
- AMS 5643 / ASTM A564
- heat treatment
- H1025
- grade
- UNS S41003
- standard
- ASTM A240
- heat treatment
- Sub-critical Anneal
About precipitation-hardening stainless steels
PH grades reach high strength through aging at intermediate temperatures while keeping the corrosion resistance of austenitic or martensitic grades. 17-4 PH and 15-5 PH are the common bar and forging stocks for aerospace and pump shafts. Mechanical properties depend strongly on the aging condition (H900, H1025, H1150).
What else is in Engineering Database
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators