AISI-H13-Hot-Work-Steel-Hardened-Tempered-538C — Tool Steel
- Category
- Tool Steel
- Material Id
- AISI H13 Hot Work Steel Hardened Tempered 538C
- Brinell Hardness (HB)
- 512
- Cte per K (1/K)
- 0.00001
- Density Kg M3 (kg/m3)
- 7,800
- Elastic Modulus MPa (MPa)
- 215,000
- Grade
- H13
- Heat Treatment
- Hardened+Tempered 538C
- Melting Point C (°C)
- 1,427
- Name
- AISI H13 Hot-Work Tool Steel (Hardened+Tempered 538C)
- Poisson Ratio (dimensionless)
- 0.285
- Reduction Percent (%)
- 50
- Specific Heat J kgK (J/(kg·K))
- 460
- Standard
- ASTM A681
- Tensile Strength MPa (MPa)
- 1,590
- Thermal Conductivity W mK (W/(m·K))
- 28.6
- Yield Strength MPa (MPa)
- 1,380
Source: ASTM A681