SAE-442-Stainless-Steel-Annealed-at-815-C-1500-F-and-Cold-Worked — Stainless Steel
- Category
- Stainless Steel
- Material Id
- SAE 442 Stainless Steel Annealed at 815 °C 1500 °F and Cold Worked
- Brinell Hardness (HB)
- 191
- Cte per K (1/K)
- 0.000011
- Density Kg M3 (kg/m3)
- 7,850
- Elastic Modulus MPa (MPa)
- 193,000
- Elongation Percent (%)
- 35.5
- Grade
- 442
- Heat Treatment
- Annealed at 815 °C (1500 °F) and Cold Worked
- Melting Point C (°C)
- 1,480
- Name
- SAE 442 Stainless Steel (Annealed at 815 °C (1500 °F) and Cold worked)
- Poisson Ratio (dimensionless)
- 0.3
- Reduction Percent (%)
- 79
- Shear Modulus MPa (MPa)
- 74,230.8
- Specific Heat J kgK (J/(kg·K))
- 460
- Standard
- SAE
- Tensile Strength MPa (MPa)
- 545
- Thermal Conductivity W mK (W/(m·K))
- 25
- Yield Strength MPa (MPa)
- 427
Source: SAE