Steel-20-Gost-1050-88-Gost-Annealing-Or-High-Tempering — Carbon Steel
- Category
- Carbon Steel
- Material Id
- Steel 20 Gost 1050-88 Gost Annealing Or High Tempering
- Brinell Hardness (HB)
- 163
- Cte per K (1/K)
- 0.000012
- Density Kg M3 (kg/m3)
- 7,859
- Elastic Modulus MPa (MPa)
- 212,000
- Elongation Percent (%)
- 21
- Heat Treatment
- Annealing Or High Tempering
- Melting Point C (°C)
- 1,480
- Name
- Steel 20 Gost 1050-88
- Poisson Ratio (dimensionless)
- 0.29
- Shear Modulus MPa (MPa)
- 82,000
- Specific Heat J kgK (J/(kg·K))
- 457
- Standard
- Gost
- Tensile Strength MPa (MPa)
- 390
- Thermal Conductivity W mK (W/(m·K))
- 65.4
- Yield Strength MPa (MPa)
- 240
Source: GOST