SAE-9255-Carbon-Steel-Oi-I-Quenched-From-885-C-1625-F-and-Tempered-at-540-C — Carbon Steel
- Category
- Carbon Steel
- Material Id
- SAE 9255 Carbon Steel Oi I Quenched From 885 °C 1625 °F and Tempered at 540 °C
- Brinell Hardness (HB)
- 321
- Cte per K (1/K)
- 0.000012
- Density Kg M3 (kg/m3)
- 7,850
- Elastic Modulus MPa (MPa)
- 200,000
- Elongation Percent (%)
- 16.7
- Grade
- 9255
- Heat Treatment
- Oi I Quenched From 885 °C (1625 °F) and Tempered at 540 °C (1000 °F)
- Melting Point C (°C)
- 1,480
- Name
- SAE 9255 Carbon Steel (Oi I Quenched From 885 °C (1625 °F) and Tempered at 540 °C ()
- Poisson Ratio (dimensionless)
- 0.3
- Reduction Percent (%)
- 38.3
- Shear Modulus MPa (MPa)
- 76,923.1
- Specific Heat J kgK (J/(kg·K))
- 466
- Standard
- SAE
- Tensile Strength MPa (MPa)
- 1,130
- Thermal Conductivity W mK (W/(m·K))
- 51.9
- Yield Strength MPa (MPa)
- 924
Source: SAE