SAE-8650-Carbon-Steel-Oil-Quenched-From-800-C-1475-F-and-Tempered-at-540-C-1 — Carbon Steel
- Category
- Carbon Steel
- Material Id
- SAE 8650 Carbon Steel Oil Quenched From 800 °C 1475 °F and Tempered at 540 °C 1
- Brinell Hardness (HB)
- 352
- Cte per K (1/K)
- 0.000012
- Density Kg M3 (kg/m3)
- 7,850
- Elastic Modulus MPa (MPa)
- 200,000
- Elongation Percent (%)
- 14.5
- Grade
- 8650
- Heat Treatment
- Oil Quenched From 800 °C (1475 °F) and Tempered at 540 °C (1000 T)
- Melting Point C (°C)
- 1,480
- Name
- SAE 8650 Carbon Steel (Oil Quenched From 800 °C (1475 °F) and Tempered at 540 °C (1)
- Poisson Ratio (dimensionless)
- 0.3
- Reduction Percent (%)
- 49.1
- Shear Modulus MPa (MPa)
- 76,923.1
- Specific Heat J kgK (J/(kg·K))
- 465
- Standard
- SAE
- Tensile Strength MPa (MPa)
- 1,185
- Thermal Conductivity W mK (W/(m·K))
- 51.9
- Yield Strength MPa (MPa)
- 1,105
Source: SAE