SAE-8630-Carbon-Steel-Water-Quenched-From-845-C-1550-T-and-Tempered-at-540-C — Carbon Steel
- Category
- Carbon Steel
- Material Id
- SAE 8630 Carbon Steel Water Quenched From 845 °C 1550 T and Tempered at 540 °C
- Brinell Hardness (HB)
- 269
- Cte per K (1/K)
- 0.000012
- Density Kg M3 (kg/m3)
- 7,850
- Elastic Modulus MPa (MPa)
- 200,000
- Elongation Percent (%)
- 18.7
- Grade
- 8630
- Heat Treatment
- Water Quenched From 845 °C (1550 T) and Tempered at 540 °C (1000 T)
- Melting Point C (°C)
- 1,480
- Name
- SAE 8630 Carbon Steel (Water Quenched From 845 °C (1550 T) and Tempered at 540 °C ()
- Poisson Ratio (dimensionless)
- 0.3
- Reduction Percent (%)
- 59.6
- Shear Modulus MPa (MPa)
- 76,923.1
- Specific Heat J kgK (J/(kg·K))
- 460
- Standard
- SAE
- Tensile Strength MPa (MPa)
- 931
- Thermal Conductivity W mK (W/(m·K))
- 51.9
- Yield Strength MPa (MPa)
- 850
Source: SAE