SAE-8620-Carbon-Steel-Annealed-at-870-C-1600-F — Carbon Steel
- Category
- Carbon Steel
- Material Id
- SAE 8620 Carbon Steel Annealed at 870 °C 1600 °F
- Brinell Hardness (HB)
- 149
- Cte per K (1/K)
- 0.000012
- Density Kg M3 (kg/m3)
- 7,850
- Elastic Modulus MPa (MPa)
- 200,000
- Elongation Percent (%)
- 31.3
- Grade
- 8620
- Heat Treatment
- Annealed at 870 °C (1600 °F)
- Melting Point C (°C)
- 1,480
- Name
- SAE 8620 Carbon Steel (Annealed at 870 °C (1600 °F))
- Poisson Ratio (dimensionless)
- 0.3
- Reduction Percent (%)
- 62.1
- Shear Modulus MPa (MPa)
- 76,923.1
- Specific Heat J kgK (J/(kg·K))
- 457
- Standard
- SAE
- Tensile Strength MPa (MPa)
- 540
- Thermal Conductivity W mK (W/(m·K))
- 51.9
- Yield Strength MPa (MPa)
- 385
Source: SAE