SAE-5150-Carbon-Steel-Oil-Quenched-From-830-C-1525-T-and-Tempered-at-540-C-10 — Carbon Steel
- Category
- Carbon Steel
- Material Id
- SAE 5150 Carbon Steel Oil Quenched From 830 °C 1525 T and Tempered at 540 °C 10
- Brinell Hardness (HB)
- 311
- Cte per K (1/K)
- 0.000012
- Density Kg M3 (kg/m3)
- 7,850
- Elastic Modulus MPa (MPa)
- 200,000
- Elongation Percent (%)
- 16.4
- Grade
- 5150
- Heat Treatment
- Oil Quenched From 830 °C (1525 T) and Tempered at 540 °C (1000 °F)
- Melting Point C (°C)
- 1,480
- Name
- SAE 5150 Carbon Steel (Oil Quenched From 830 °C (1525 T) and Tempered at 540 °C (10)
- Poisson Ratio (dimensionless)
- 0.3
- Reduction Percent (%)
- 52.9
- Shear Modulus MPa (MPa)
- 76,923.1
- Specific Heat J kgK (J/(kg·K))
- 465
- Standard
- SAE
- Tensile Strength MPa (MPa)
- 1,055
- Thermal Conductivity W mK (W/(m·K))
- 51.9
- Yield Strength MPa (MPa)
- 1,000
Source: SAE