SAE-4340-Carbon-Steel-Oil-Quenched-From-800-C-1475-T-and-Tempered-at-540-C-10 — Carbon Steel
- Category
- Carbon Steel
- Material Id
- SAE 4340 Carbon Steel Oil Quenched From 800 °C 1475 T and Tempered at 540 °C 10
- Brinell Hardness (HB)
- 352
- Cte per K (1/K)
- 0.000012
- Density Kg M3 (kg/m3)
- 7,850
- Elastic Modulus MPa (MPa)
- 200,000
- Elongation Percent (%)
- 14.2
- Grade
- 4340
- Heat Treatment
- Oil Quenched From 800 °C (1475 T) and Tempered at 540 °C (1000 T)
- Melting Point C (°C)
- 1,480
- Name
- SAE 4340 Carbon Steel (Oil Quenched From 800 °C (1475 T) and Tempered at 540 °C (10)
- Poisson Ratio (dimensionless)
- 0.3
- Shear Modulus MPa (MPa)
- 76,923.1
- Specific Heat J kgK (J/(kg·K))
- 462
- Standard
- SAE
- Tensile Strength MPa (MPa)
- 1,207
- Thermal Conductivity W mK (W/(m·K))
- 51.9
- Yield Strength MPa (MPa)
- 1,145
Source: SAE