Ti-6Al-4V vs Ti-6Al-6V-2Sn Bar Solution Treated and Aged
Property comparison of Ti-6Al-4V and Ti-6Al-6V-2Sn Bar Solution Treated and Aged, both titanium alloy.
| Property | Ti-6Al-4V | Ti-6Al-6V-2Sn Bar Solution Treated and Aged | Difference |
|---|---|---|---|
| Yield strength | 880 MPa | 1,103 MPa | +25% |
| Tensile strength | 950 MPa | 1,207 MPa | +27% |
| Elongation | 14 % | 8 % | -43% |
| Elastic modulus | 114,000 MPa | 110,316 MPa | -3% |
| Shear modulus | 44,000 MPa | 42,748 MPa | -3% |
| Poisson ratio | 0.342 | 0.31 | -9% |
| Density | 4,430 kg/m³ | 4,540 kg/m³ | +2% |
Difference is Ti-6Al-6V-2Sn Bar Solution Treated and Aged relative to Ti-6Al-4V. Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
- grade
- Ti-6Al-4V
- standard
- ASTM
- heat treatment
- Annealed
- grade
- Ti-6Al-6V-2Sn
- standard
- MIL-HDBK-5J
- heat treatment
- Solution Treated and Aged
What else is in Engineering Database
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators