ATI 601 (UNS N06601) vs ATI 720 (Ni-Cr-Co-Mo-W-Ti-Al precipitation-hardened superalloy)
Property comparison of ATI 601 (UNS N06601) and ATI 720 (Ni-Cr-Co-Mo-W-Ti-Al precipitation-hardened superalloy), both nickel alloy.
| Property | ATI 601 (UNS N06601) | ATI 720 (Ni-Cr-Co-Mo-W-Ti-Al precipitation-hardened superalloy) | Difference |
|---|---|---|---|
| Yield strength | 250 MPa | 1,207 MPa | +383% |
| Tensile strength | 670 MPa | 1,586 MPa | +137% |
| Elongation | 55 % | 18 % | -67% |
| Elastic modulus | 205,000 MPa | 220,000 MPa | +7% |
| Density | 8,050 kg/m³ | 8,090 kg/m³ | 0% |
Difference is ATI 720 (Ni-Cr-Co-Mo-W-Ti-Al precipitation-hardened superalloy) relative to ATI 601 (UNS N06601). Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
- grade
- N06601
- standard
- ATI Technical Data Sheet
- heat treatment
- Solution Treated 1149C (2100F)
- grade
- Proprietary (Rolls Royce MSRR7252 / GE C50TF105)
- standard
- ATI Technical Data Sheet
- heat treatment
- Solution treat 1080-1100°C/4h OQ + age 650°C/24h AC + 760°C/16h AC
What else is in Engineering Database
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators