Aluminum Alloy 3105-H25 vs Aluminum Alloy Alclad 3003-H16
Property comparison of Aluminum Alloy 3105-H25 and Aluminum Alloy Alclad 3003-H16, both aluminum alloy.
| Property | Aluminum Alloy 3105-H25 | Aluminum Alloy Alclad 3003-H16 | Difference |
|---|---|---|---|
| Yield strength | 159 MPa | 172 MPa | +8% |
| Tensile strength | 179 MPa | 179 MPa | 0% |
| Elongation | 8 % | 5 % | -38% |
| Elastic modulus | 73,000 MPa | 73,000 MPa | 0% |
| Shear modulus | 26,000 MPa | 26,000 MPa | 0% |
| Poisson ratio | 0.33 | 0.33 | 0% |
| Density | 2,700 kg/m³ | 2,700 kg/m³ | 0% |
| Thermal conductivity | 159 W/m·K | 159 W/m·K | 0% |
| Specific heat | 893 J/kg·K | 893 J/kg·K | 0% |
| Coefficient of thermal expansion | 0.000023 1/K | 0.000023 1/K | 0% |
| Melting point | 629 °C | 629 °C | 0% |
Difference is Aluminum Alloy Alclad 3003-H16 relative to Aluminum Alloy 3105-H25. Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
- standard
- ANSI
- heat treatment
- Wrought
- standard
- ANSI
- heat treatment
- Wrought
About 3xxx aluminum alloys
3xxx aluminum alloys carry manganese as the main alloying element. They are not heat-treatable and offer moderate strength with good formability and corrosion resistance. 3003 is the most common general-purpose sheet; 3004 is used for beverage can bodies.
What else is in Engineering Database
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators