7050 vs 7150
Property comparison of 7050 and 7150, both aluminum alloy.
| Property | 7050 | 7150 | Difference |
|---|---|---|---|
| Yield strength | 434 MPa | 544.7 MPa | +26% |
| Tensile strength | 496 MPa | 586.07 MPa | +18% |
| Elongation | 12 % | 9 % | -25% |
| Elastic modulus | 73,000 MPa | 70,329 MPa | -4% |
| Shear modulus | 26,000 MPa | 26,891 MPa | +3% |
| Poisson ratio | 0.33 | 0.33 | 0% |
| Density | 2,700 kg/m³ | 2,823 kg/m³ | +5% |
Difference is 7150 relative to 7050. Values are taken from the representative row of each material; both materials may have multiple heat treatments or conditions on their individual pages.
Identification
- standard
- ANSI
- heat treatment
- Wrought
- grade
- —
- standard
- MIL-HDBK-5J
- heat treatment
- Wrought
- grade
- 7150
About 7xxx aluminum alloys
7xxx aluminum alloys are alloyed with zinc and reach the highest strengths in the wrought family. Weldability is poor and corrosion resistance trails 5xxx and 6xxx. 7075 is the aerospace standard for highly loaded structure; 7050 trades a small amount of strength for better fracture toughness.
What else is in Engineering Database
AI built for engineering. Searches the engineering database, performs calculations, gives source-backed engineering insights.
Get started for free ↗Reference Data375 engineering tablesMaterial properties, pipe and shape dimensions, code tables, and electrical ratings across mechanical, civil, chemical, electrical, materials, and manufacturing engineering.
Browse dataCalculatorsDeterministic engineering calculatorsSizing, checking, and conversion tools that run against the reference tables. Inputs are code-compliant, outputs are traceable to the source standard.
Browse calculators